中温回火（250－500度）中温回火所得组织为回火屈氏体。其目的是获得高的屈服强度，弹性极限和较高的韧性。

Medium temperature tempering (250-500 degrees)， medium temperature tempering income group as tempered troostite. Its is to obtain high yield strength， elastic limit and high toughness.

因此，它主要用于各种GB/T9711.1搪瓷管和热作模具的处理，回火后硬度一般为HRC35－50。

Therefore， it is mainly used for various kinds of GB/T9711.1 enamel tube and hot mould processing， after tempering hardness is HRC35-50 commonly.

低温回火（150－250度）低温回火所得组织为回火马氏体。其目的是在保持淬火钢的高硬度和高耐磨性的前提下，降低其淬火内应力和脆性，以免使用时崩裂或过早损坏。

Low temperature tempering (150-250 degrees)， low temperature tempering the organization for the tempered martensite. Its aim is to keep a hardened steel under the premise of high hardness and high wear resistance， decrease the quenching stress and brittleness， lest when using split or premature failure.

它主要用于各种高碳的切削刃具，搪瓷管长度，量具，GB/T9711.1搪瓷管，滚动轴承以及渗碳件等，回火后硬度一般为HRC58－64。

It is mainly used for cutting all kinds of high carbon cutting， measuring tool， GB/T9711.1 enamel tube，搪瓷管光泽度， such as pieces of rolling bearing and carburizing， after tempering hardness is commonly HRC58-64.

搪瓷烧成方法

一般沿用传统的搪瓷炉来烧成，即在一具有保温隔热墙的固定空间里布置加热设备，然后将待搪瓷的工件放置于这个空间里面一定时间，待工件表面的搪瓷涂层熔融烧结后再将其取出，搪瓷管价格，这一传统的搪瓷烧成方法的设备有箱式电阻炉、连续式电加热搪瓷隧道炉、连续式燃气搪瓷隧道炉等。一般长度不太长的钢管表面搪瓷烧成也可以采用这种传统的方法。但是要是搪瓷钢管长度很长，超过3米以后，这种钢管表面烧搪瓷就变得困难，因为一般搪瓷炉设计时所能烧成的工件高度一般不超过2米，炉子过高在垂直方向的温度差异会加大，不利于搪瓷烧成，而类似于钢管这种细长条状的待搪瓷工件，如果在烧成时垂直吊挂，则对其变形(主要是变形变曲)不会有什么影响，而一旦将钢管这种形状的工件水平吊挂来烧成，则钢管变曲严重，无法制作合格的钢管搪瓷产品，钢管长度超3米后，利用传统的搪瓷炉来烧成搪瓷的话，只能水平吊挂，烧成温度高达860°C，搪瓷管，这样钢管在烧成中的变形是没法控制的。虽然现在有专门设计的井式炉来烧成类似于钢管这种特殊工件，井式炉只是将做传统箱式炉的高度加大来满足钢管垂直吊挂的要求，但其垂直方向的温度差的控制依然成问题。